17 January 2017
17 January 2017
Sicomin has supplied a complete package of composite materials to produce both moulds and parts for the 5 gilded domes of the recently inaugurated Russian Orthodox Cathedral in Paris.
Working alongside Multiplast (part of the Carboman Group), main contractor Bouygues and engineering consultants Calcul Méca, Sicomin says it was able to support in realising architect Jean-Michel Wilmotte’s stunning contemporary design for the Russian Orthodox Cultural and Spiritual Centre in central Paris.
Sicomin supplied materials for the dome tooling to Décision, a Swiss based Carboman Group company, who infused a set of glass fibre multiaxial fabric and balsa reinforced moulds using Sicomin’s SR8100 / SD7820 cost effective 120°C Tg epoxy infusion system.
It explains that the dome panels themselves were produced at Multiplast’s factory in Vannes, France using Sicomin’s SR8100 / SD4772 epoxy infusion system and a specially developed glass fibre reinforcement lay-up. By combining their heavyweight quadaxial fabric style QX1180 with a woven 500gsm fabric, Sicomin was able to provide a laminate with no print through and excellent top surface flow characteristics to prevent dry spots.
Using a Sicomin composite material solution for the domes had many advantages for this project. The domes light weight allowed for rapid installation as well as reducing the dead loads that must be carried by the building structure. Another benefit of building the domes off site, was that both manufacture and decoration of the domes could be carried out in controlled conditions without the weather impacting the production process. Sicomin carried out extensive DSC testing in their laboratory to optimise the post curing procedure to ensure the stability of the finished parts before craftsmen applied 86,000 leaves of real gold to the 640m2 surface area of the domes.
Sicomin will be exhibiting at the next European CompIC conference and exhibition in Amsterdam from 31st January to 1st February 2017. Please visit them at this event to learn more about Sicomin’s complete composite materials packages for global construction and civil engineering projects.
Photo provided by Sicomin
The University of Southern Queensland’s (USQ) Centre for Future Materials (CFM) has partnered with Joinlox to investigate a prefabricated composite repair system with an easy-fit and self-locking mechanical joint called PileJax.
Federal-Mogul Powertrain's self-lubricating deva.tex 552 Marine composite bearing material has been certified by ship and offshore classification society DNV GL.
SAERTEX reports that it has contributed to the prototype production of a wind turbine blade with probably the longest and thickest carbon fibre spar cap made in vacuum infusion technology so far.