Blades for Rooftop Wind Turbine Manufactured from Composites Evolution’s Biotex Flax

11 March 2014

Blades for Rooftop Wind Turbine Manufactured from Composites Evolution’s Biotex Flax

Composites Evolution’s Biotex Flax has been used to manufacture natural fibre reinforced blades for a rooftop wind turbine at the University of Stuttgart.

According to Composites Evolution, the blades were conceived, designed and manufactured by the SWE (Endowed Chair of Wind Energy) at the University, the team having found that Biotex Flax reinforcement’s unique twistless technology gave them the performance characteristics that they were looking for.

SWE’s research is focused on improving the reliability of turbines whilst reducing the production costs of wind energy. It started design in 2011, with the aim of constructing new rotor blades for the university’s 1kW rooftop wind turbine. After a trip to “The Eden Project” in the UK, the team wanted to familiarise themselves with natural fibres and contacted Composites Evolution to test the performance of its Biotex materials.

Composites Evolution explains that along with a range of other materials, the fibres were tested with different resins to validate their performance characteristics. SWE found that Composites Evolution’s Biotex Flax correlated best with the performance they expected and it felt they had a good data basis to make a lightweight and stiff natural fibre blade.

The blade, consisting of Biotex Flax 2x2 twill 400gsm as the main shell and Biotex Flax unidirectional 275gsm used for the blade’s belt and root, was built in two halves. Both were hand-laminated and then vacuum-bagged in two female moulds. The two separate halves were then joined using Momentive’s RIM 235 epoxy resin.

Once completed the blades were assembled onto the rooftop turbine for performance tests. SWE says it plans to use the blades in further tests focusing on their strength performance compared to blades constructed from other materials. A fourth blade was embedded with strain gauges and the team will be comparing the results to standard carbon and glass blades.

The completed blade is being displayed at JEC Paris this week, 11th 13th March, on the Composites Evolution stand, Hall 7.2, stand E6.

Photo provided by Composites Evolution






Related / You might like...

Compcut 200 Increases Testing Productivity at Renault Sport Racing

Sharp & Tappin has installed and commissioned a Compcut 200 composite plate saw at Renault Sport Racing in Enstone, Oxfordshire, UK.

Electric GT’s Tesla P100DL Features Bcomp Flax Fibre Technologies

Electric GT Holdings and SPV Racing recently unveiled the race-ready version of the EPCS V2.3 Tesla P100DL at Circuit de Barcelona-Catalunya. The car features lightweight body parts made using Bcomp's ampliTex and powerRibs natural fibre composite reinforcement products, contributing to a 500 kg weight reduction over the road edition.

Codem Composites Supports Sahara Force India F1 Team

UK company Codem Composites has provided key bodywork components to support the F1 team Sahara Force India.